Carbon nanotube array and method for making same

ABSTRACT

A carbon nanotube-based device ( 40 ) includes a substrate ( 10 ), a number of catalytic nano-sized particles ( 131 ) formed on the substrate, and an aligned carbon nanotube array ( 15 ) extending from the alloy catalytic nano-sized particles. The aligned carbon nanotube array progressively bends in a predetermined direction. A method for making the carbon nanotube-based device includes the steps of: providing a substrate; depositing a layer of catalyst on the substrate; depositing a layer of catalyst-doped material on the catalyst layer, for varying a reaction rate of synthesis of the aligned carbon nanotube array; annealing the catalyst and the catalyst-doped material in an oxygen-containing gas at a low temperature; and exposing the nano-sized particles and catalyst-doped material to a carbon-containing source gas at a predetermined temperature such that the aligned carbon nanotube array grows from the substrate.

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The present invention relates to carbon nanotube-based devices and methods for making such devices. The application relates to a contemporaneously filed application titled “CARBON NANOTUBE-BASED DEVICE AND METHOD FOR MAKING THE SAME” and having the same applicants and the same assignee with the instant application.

[0003] 2. Description of Related Art

[0004] Carbon nanotubes have electrical conductance relate to their structure and chemically stable. Carbon nanotubes typically have very small diameters (less than 100 nanometers) and large aspect ratios (length/diameter). Due to these and other properties, it has been suggested that carbon nanotubes will play an important role in fields such as nano-scale integrate circuits, field emission, and single electronic components such as single electronic transistors. Recently, some electronic components based on a single carbon nanotube have been made in laboratories, such components including a field effect transistor, a logic circuit and a memory. The characteristics of these components are being actively researched. For example, a nanotube transistor is reported in an article by Sander J Tans et al. entitled “Room-temperature transistor based on a single carbon nanotube” (Nature 393-49, 1998). However, synthesis of large amounts of carbon nanotubes having practical applications depends in large part on manufacturing techniques developed using a bottom-up approach.

[0005] Manufacturing techniques using the bottom-up approach can control the position, direction, and size of carbon nanotubes. Desired configurations for target nano-scale components can be obtained using relatively few and relatively economical formation steps. A method of controlling the position of carbon nanotube growth by distributing a patterned catalyst is reported in an article by Fan S. S. et al. entitled “Self-oriented regular [sic] of carbon nanotubes and their field emission properties” (Science Vol. 283, pp.512-514, Jan. 22, 1999). In said method, the obtained carbon nanotubes extend perpendicularly to a plane of a substrate.

[0006] In addition, a method for controlling the growth of aligned nanotubes in several directions in a single process is reported by B. Q. Wei et al. in an article entitled “Organized assembly of carbon nanotubes” (Nature Vol. 416, pp.495-496, Apr. 4, 2002).

[0007] However, in all the above-mentioned methods, it is not possible to properly control a direction in which the aligned nanotubes extend.

[0008] A method to control the direction of single-walled carbon nanotube growth is reported in an article by Yue-gang Zhang et al. entitled “Electric-field-directed growth of aligned single-walled carbon nanotubes” (Applied Physics Letters, Vol. 79, Number 19, Nov. 5, 2001).

[0009] However, Zhang et al. method was a wide area control, all the carbon nanotubes in a particular region tend to growth in the same direction as that of the electric field. It is difficult to realize localized and versatile direction control by any external field like an electric field. This limits the diversified design of carbon nanotube-based structures.

SUMMARY OF THE INVENTION

[0010] Accordingly, an object of the present invention is to provide a carbon nanotube-based device having an aligned carbon nanotube array that progressively bends in a predetermined direction.

[0011] Another object of the present invention is to provide a method for localized control of nanotube array's orientation and bending.

[0012] Another object of the present invention is to provide a method for making a carbon nanotube-based device having an aligned carbon nanotube array that progressively bends in a predetermined direction.

[0013] In order to achieve the objects set out above, the present invention provides a method for making a carbon nanotube-based device. The method is able to control a direction of growth of a carbon nanotube array, and comprises the steps of: (1) providing a substrate; (2) depositing a layer of catalyst on the substrate; (3) depositing a layer of catalyst-doped material on the catalyst layer, for varying a reaction rate of synthesis of an aligned carbon nanotube array; (4) annealing the catalyst and the catalyst-doped material in an oxygen-containing gas at a low temperature; and (5) exposing the nano-sized particles and catalyst-doped material to a carbon-containing source gas at a predetermined temperature such that the aligned carbon nanotube array grows from the substrate.

[0014] Other objects, advantages and novel features of the present invention will become more apparent from the following detailed description and claims, and from the accompanying drawings, in which:

BRIEF DESCRIPTION OF THE DRAWINGS

[0015]FIG. 1 is a schematic side elevation view of a substrate with a catalyst layer deposited thereon, in accordance with a preferred method of the present invention for making a carbon nanotube-based device;

[0016]FIG. 2 is similar to FIG. 1, but showing a catalyst-doped material layer being deposited on the catalyst layer in accordance with said preferred method;

[0017]FIG. 3 is similar to FIG. 2, but showing the treated substrate after annealing, heating and exposure to protective and carbon—containing source gases in accordance with said preferred method, wherein the catalyst-doped material and the catalyst have changed into alloy catalytic nano-sized particles; and

[0018]FIG. 4 is similar to FIG. 3, but showing aligned carbon nanotubes formed from the alloy catalytic nano-sized particles in accordance with said preferred method.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENT OF THE INVENTION

[0019] Reference will now be made to the drawings to describe the present invention in detail.

[0020] Referring to FIG. 4, a carbon nanotube-based device 40 in accordance with a preferred embodiment of the present invention comprises a substrate 10, a plurality of alloy catalytic nano-sized particles 131 formed on the substrate 10, and an aligned carbon nanotube array 15 extending from the alloy catalytic nano-sized particles 131. The aligned carbon nanotube array 15 progressively bends in a predetermined direction.

[0021] Referring to FIGS. 1-4, a preferred method of the present invention for making the carbon nanotube-based device 40 is as follows:

[0022] First, a substrate 10 is provided, which may be selected from the group consisting of silicon, quartz and glass. A photo-resist layer 11 is formed on the substrate 10. A catalyst layer 13 is deposited on the substrate 10 by electron-beam (e-beam) evaporation or thermal evaporation. The catalyst layer 13 must have a uniform thickness, preferably in the range from 2 nanometers to 10 nanometers. A material of the catalyst layer 13 can be selected from the group consisting of iron, cobalt, nickel, or any suitable combination alloy thereof. In the preferred method, iron is selected as the material of the catalyst layer 13, and is deposited on the surface of the substrate 10 to a uniform thickness of 6 nanometers.

[0023] A catalyst-doped material layer 121 is then deposited on the catalyst layer 13. A linear evaporation source 12 is disposed above the photo-resist layer 11. An end of the linear evaporation source 12 and an inner surface (not labeled) of the photo-resist layer 11 share a common vertical plane. The catalyst-doped material layer 121 is deposited on the catalyst layer 13 by thermal evaporation. The thickness of the catalyst-doped material layer 121 is preferably in the range from zero to 10 nanometers, and gradually decreases along a given direction.

[0024] The catalyst-doped material layer 121 is capable of varying reaction rates of synthesis of carbon nanotubes. A content of catalyst-doped material in the catalyst-doped material layer 121 determines a particular reaction rate of synthesis of carbon nanotubes. In the preferred method, the catalyst-doped material is copper, which is capable of providing a decreased reaction rate of synthesis of carbon nanotubes.

[0025] Alternatively, the linear evaporation source 12 may be substituted by a point evaporation source that moves along a pre-defined line. Furthermore, the above-described method of depositing the catalyst-doped material layer 121 may alternatively employ other techniques such as e-beam evaporation. Moreover, the catalyst-doped material can be selected from group of cobalt, nickel, molybdenum, ruthenium, manganese or a combination of the materials thereof.

[0026] . . . The treated substrate 10 is then annealed in an oxygen-containing gas at a low temperature for 10 hours until the catalyst layer 13 is oxidized and changed into separate nano-sized particles (not shown). Preferably, said low temperature is in the range from 200° C. to 400° C. The treated substrate 10 is then placed in a furnace (not shown). The furnace is heated up to a predetermined temperature in a flowing protective gas. The predetermined temperature may vary according to the type of catalyst layer 13 used. In the preferred method, iron is used as the catalyst layer 13, and the predetermined temperature is in the range from 600° C. to 700° C. The protective gas can be selected from the group consisting of noble gases and nitrogen. Preferably, argon is used as the protective gas. A carbon source gas is then introduced into the furnace. In the preferred method, acetylene is used as the carbon source gas. From the time the carbon source gas is introduced, the separate nano-sized particles and the catalyst-doped material layer 121 cooperatively form the alloy catalytic nano-sized particles 131, and the aligned carbon nanotube array 15 grows from the alloy catalytic nano-sized particles 131.

[0027] The alloy catalytic nano-sized particles 131 are larger at a region corresponding to the thick end of the catalyst-doped material layer 121, said thick end having a higher content of the catalyst-doped material. Correspondingly, the alloy catalytic nano-sized particles 131 are smaller at a region corresponding to the thin end of the catalyst-doped material layer 121, said thin end having a lower content of the catalyst-doped material. A change in the content of the alloy catalytic nano-sized particles 131 is gradual from said region corresponding to said thick end to said region corresponding to said thin end.

[0028] Accordingly, respective growth rates of carbon nanotube from the alloy catalytic nano-sized particles 131 gradually increase from said region corresponding to said thick end through to said region corresponding to said thin end. Thus the aligned carbon nanotube array 15 extending from the alloy catalytic nano-sized particles 131 gradually bends toward said region corresponding to said thick end, due to van der Waals forces acting between the neighboring carbon nanotubes.

[0029] It will be apparent to those having ordinary skill in the field of the present invention that the above-described order of deposition of the catalyst layer 13 and the catalyst-doped material layer 121 may be reversed. If this is done, the aligned carbon nanotube array 15 with progressive bending in the predetermined direction is still attained.

[0030] It will be further apparent to those having ordinary skill in the field of the present invention: that the acetylene gas may be substituted with methane, ethane or another similar hydrocarbon gas; that the argon gas may be substituted with nitrogen, helium or another similar protective gas; and that the catalyst layer 13 of iron may be substituted with cobalt, nickel, molybdenum, ruthenium, manganese, or a combination or alloy thereof.

[0031] The aligned carbon nanotube array 15 of the present invention can be used in applications such as flat panel displays, nano-electronics, and cathode electron guns having high field current emission.

[0032] It is understood that the invention may be embodied in other forms without departing from the spirit thereof. Thus, the present examples and embodiments are to be considered in all respects as illustrative and not restrictive, and the invention is not to be limited to the details given herein. 

What is claimed is:
 1. A carbon nanotube-based device comprising: a substrate; a plurality of alloy catalytic nano-sized particles formed on the substrate; and an aligned carbon nanotube array extending from the alloy catalytic nano-sized particles and progressively bending in a predetermined direction; wherein said alloy catalytic nano-sized particles each comprise a catalyst material and a catalyst-doped material, the catalyst-doped material being capable of varying a reaction rate of synthesis of carbon nanotubes of the carbon nanotube array.
 2. The carbon nanotube-based device as claimed in claim 1, wherein the substrate comprises silicon, quartz or glass.
 3. The carbon nanotube-based device as claimed in claim 1, wherein the catalyst material is selected from the group consisting of iron, cobalt, nickel, molybdenum, ruthenium, manganese, and any suitable combination alloy thereof.
 4. The carbon nanotube-based device as claimed in claim 1, wherein the catalyst-doped material comprises copper, molybdenum, or a combination of copper and molybdenum.
 5. The carbon nanotube-based device as claimed in claim 1, wherein said catalyst-doped material is capable of either increasing or decreasing growing rates of said carbon nanotubes of the carbon nanotube array.
 6. The carbon nanotube-based device as claimed in claim 1, wherein said catalyst-doped material gradually increases or decreases along another predetermined direction on said substrate.
 7. The carbon nanotube-based device as claimed in claim 1, wherein said catalyst-doped material is in a form of layer, and said layer is either thickened or thinned along another predetermined direction on said substrate.
 8. A method for making a carbon nanotube-based device, the method comprising the steps of: providing a substrate; depositing a layer of catalyst on the substrate; depositing a layer of catalyst-doped material on the catalyst layer for varying a reaction rate of synthesis of carbon nanotubes; annealing the catalyst and the catalyst-doped material in an oxygen-containing gas at a low temperature; and exposing the nano-sized particles and catalyst-doped material to a carbon-containing source gas at a predetermined temperature such that an aligned carbon nanotube array grows from the substrate.
 9. The method in accordance with claim 8, wherein the substrate comprises silicon, glass or quartz.
 10. The method in accordance with claim 8, wherein a material of the catalyst layer is selected from the group consisting of iron, cobalt, nickel, and any suitable combination alloy thereof.
 11. The method in accordance with claim 8, wherein a thickness of the catalyst layer on the substrate is uniform, and is in the range from 2 nanometers to 10 nanometers.
 12. The method in accordance with claim 8, wherein the catalyst-doped material comprises cobalt, nickel, molybdenum, copper, ruthenium, manganese or a combination of the materials thereof.
 13. The method in accordance with claim 8, wherein a thickness of the catalyst-doped material layer is less than or equal to 10 nanometers.
 14. The method in accordance with claim 8, wherein a thickness of the catalyst-doped material layer gradually decreases along a given direction.
 15. The method in accordance with claim 9, wherein the depositing of the catalyst-doped material layer is performed by electron-beam evaporation deposition or thermal evaporation.
 16. The method in accordance with claim 15, wherein an evaporation source of the thermal evaporation deposition is a linear evaporation source.
 17. The method in accordance with claim 15, wherein an evaporation source of the thermal evaporation deposition is a point evaporation source moving along a line.
 18. The method in accordance with claim 8, wherein said low temperature is in the range from 200° C. to 400° C.
 19. A carbon nanotube-based device comprising: a substrate; a plurality of alloy catalytic nano-sized particles formed on the substrate; and an aligned carbon nanotube array respectively extending from the alloy catalytic nano-sized particles with gradually respective increasing or decreasing lengths of said carbon nanotubes of the carbon nanotube array arranged along a direction on said substrate; wherein said alloy catalytic nano-sized particles each comprise a catalyst material and a catalyst-doped material, the catalyst-doped material being capable of varying a reaction rate of synthesis of carbon nanotubes of the carbon nanotube array.
 20. The carbon nanotube-based device in accordance with claim 19, wherein said catalyst-doped material increases or decreases along said direction on said substrate. 